- 阻燃
- 柔软
- 收缩温度:开始收缩温度70℃,完全收缩温度90℃
- 工作温度:-30℃~105℃
- 径向收缩比:2:1,轴向收缩率≤5%
- 良好的绝缘性、耐腐蚀性及耐候性
- 符合欧盟rohs指令要求
应用 适用于电线电缆、电子线束以及各种接线端子、连接部件、焊点处的绝缘防护和补强等。 规格尺寸 | | 规格 | 收缩前尺寸 | 收缩后尺寸 | | | 内径(Zui小) | 平均壁厚 | 内径(Zui大) | 平均壁厚 | | mm | inch | mm | inch | mm | inch | mm | inch | mm | inch | | | | | | | | | | | 0.8 | 3/64 | 0.90 | 0.035 | 0.18 | 0.007 | 0.40 | 0.016 | 0.30 | 0.012 | | 1.0 | 1/16 | 1.30 | 0.051 | 0.18 | 0.007 | 0.50 | 0.020 | 0.30 | 0.012 | | 1.5 | 3/32 | 1.80 | 0.071 | 0.20 | 0.008 | 0.75 | 0.030 | 0.40 | 0.016 | | 2.0 | 7/64 | 2.30 | 0.090 | 0.22 | 0.009 | 1.00 | 0.039 | 0.40 | 0.016 | | 2.5 | 1/8 | 2.80 | 0.110 | 0.25 | 0.010 | 1.25 | 0.049 | 0.40 | 0.016 | | 3.0 | 9/64 | 3.30 | 0.130 | 0.25 | 0.010 | 1.50 | 0.059 | 0.45 | 0.018 | | 3.5 | 5/32 | 3.80 | 0.149 | 0.25 | 0.010 | 1.75 | 0.069 | 0.45 | 0.018 | | 4.0 | 3/16 | 4.30 | 0.169 | 0.25 | 0.010 | 2.00 | 0.079 | 0.50 | 0.020 | | 4.5 | 13/64 | 5.00 | 0.197 | 0.25 | 0.010 | 2.50 | 0.098 | 0.50 | 0.020 | | 5.0 | 7/32 | 5.30 | 0.208 | 0.25 | 0.010 | 2.50 | 0.098 | 0.50 | 0.020 | | 6.0 | 1/4 | 6.30 | 0.248 | 0.25 | 0.010 | 3.00 | 0.118 | 0.55 | 0.022 | | 7.0 | 19/64 | 7.20 | 0.273 | 0.25 | 0.010 | 3.50 | 0.138 | 0.55 | 0.022 | | 8.0 | 11/32 | 8.10 | 0.317 | 0.30 | 0.012 | 4.00 | 0.157 | 0.60 | 0.024 | | 9.0 | 3/8 | 9.10 | 0.358 | 0.30 | 0.012 | 4.50 | 0.177 | 0.60 | 0.024 | | 10.0 | 13/32 | 10.10 | 0.397 | 0.30 | 0.012 | 5.00 | 0.197 | 0.60 | 0.024 | | 11.0 | 29/64 | 11.10 | 0.437 | 0.30 | 0.012 | 5.50 | 0.217 | 0.60 | 0.024 | | 12.0 | 1/ 2 | 12.10 | 0.476 | 0.30 | 0.012 | 6.00 | 0.236 | 0.60 | 0.024 | | 13.0 | 17/32 | 13.10 | 0.515 | 0.30 | 0.012 | 6.50 | 0.256 | 0.60 | 0.024 | | 14.0 | 37/64 | 14.20 | 0.559 | 0.30 | 0.012 | 7.00 | 0.276 | 0.60 | 0.024 | | 15.0 | 39/64 | 15.20 | 0.598 | 0.35 | 0.014 | 7.50 | 0.295 | 0.65 | 0.026 | | 16.0 | 21/32 | 16.30 | 0.641 | 0.35 | 0.014 | 8.00 | 0.315 | 0.65 | 0.026 | | 18.0 | 3/4 | 18.30 | 0.720 | 0.40 | 0.016 | 9.00 | 0.354 | 0.75 | 0.030 | | 20.0 | 53/64 | 20.70 | 0.815 | 0.40 | 0.016 | 10.00 | 0.394 | 0.80 | 0.031 |
|
|